1.4000
Material No
1.4000
EN/DIN
X6Cr13
410S / 1.4000 grade ferritic stainless steel is the lower carbon version of 410 grade round stainless steel. Unlike Martensitic 410 grade, 1.4000 grade stainless steel cannot be hardened.
Electrical Properties
|
Electrical Resistance
|
0.60 x10 ^ -6 Ω .m
|
|
Thermal conductivity
|
24.9 W/m-K
|
|
Maximum Temperature: Corrosion
|
390℃
|
Process Properties
|
Machinability
|
good
|
|
Hot Forming
|
good
|
|
Hardness HB
|
424
|
Thermal Recovery
|
Specific heat capacity
|
480 J/kg-K
|
|
Melting point
|
1440℃
|
The 1.4000 round stainless steel grade also corresponds to the following designations:
410S
UNS S41008
403S17
| |
Dimensions mm |
| X6Cr13 |
6mm |
up to |
50mm |
Chemical Composition
| Grade |
C |
Cr |
Mn |
P |
Si |
S |
1.4000
|
0.08 max |
14.0 max
|
1.0 max |
0.040 max |
1.0 max |
0.015 max |
Physical Composition
It is used in the construction of power plant, electricity generation, pumps, compressors and turbine wheels.
|
Density
g/cm3
|
Specific heat capacity J/kg K |
Thermal conductivity W/m K |
Electrical resistivity
Ω mm2/m
|
|
7.7
|
430 |
25 |
0.6
|
|
Hardness HB 30
≤ HB
|
0.2%Yield Strength R ≥
N/ mm2
|
Tensile strength R N/ mm2
|
Elongation A ≥ %
|
Modulus of elasticity
kN/mm2
|
|
320
|
520
|
700-800
|
15/12
|
200
|