1.4104
INT
X6CrMoS17
Electrical Properties
|
Electrical Resistance
|
0.60 x10 ^ -6 Ω .m
|
|
Hardness HB
|
Max 180
|
|
Magnetic susceptibility
|
-
|
Process Properties
|
Machinability
|
Very good
|
|
Hot Forming
|
good
|
|
Cold Forming
|
low
|
Thermal Recovery
|
Softening Annealing
|
1010-1120 ℃
30 min
|
|
Melting point
|
1430℃
|
| |
Dimensions mm |
| X6CrMoS17 |
6mm |
up to |
50mm |
Chemical Composition
| Grade |
C |
Cr |
Mn |
P |
Si |
S |
Mo |
1.4105
|
0.80 max |
14.00 max
|
1.5 max |
0.40 max |
1.0 max |
0.03 max |
0.60 max |
Physical Composition
It is used in the construction of pump shafts, motor shafts, pumps, compressors, blades are used.
|
Density
g/cm3
|
Specific heat capacity J/kg K |
Thermal conductivity W/m K |
Electrical resistivity
Ω mm2/m
|
|
7.75
|
430 |
24.9 |
0.55
|
|
Hardness HB 30
≤ HB
|
0.2%Yield Strength R ≥
N/ mm2
|
Tensile strength R N/ mm2
|
Elongation A ≥ %
|
Modulus of elasticity
kN/mm2
|
|
320
|
520
|
700-950
|
13
|
200
|