Produkte \ Rohre \ Hydraulikrohr \ X 6 CRNIMOTI 17 12 2

X 6 CRNIMOTI 17 12 2

EN/DIN

DIN 17458

  Formatte  mm
X 6 CRNIMOTI 17 12 2   6.0 x 1.0
6.0 x 1.5
6.0 x 2.0
7.0 x 1.5
8.0 x 1.0
8.0 x 1.5
8.0 x 2.0
9.0 x 1.0
10.0 x 1.0
10.0 x 1.5
10.0 x 2.0
10.0 x 2.5
11.0 x 1.0
12.0 x 1.0
12.0 x 1.50
12.0 x 2.0
12.0 x 2.50
12.0 x 3.0
13.0 x 1.5
13.0 x 2.50
13.50 x 1.60
13.50 x 2.30
13.72 x 1.65
13.72 x 2.24
14.0 x 1.0
14.0 x 1.5
14.0 x 2.0
14.0 x 2.5
14.0 x 3.0
15.0 x 1.0
15.0 x 2.5
15.0 x 3.0
16.0 x 1.0
16.0 x 1.5
16.0 x 2.0
16.0 x 2.5
16.0 x 3.0
16.0 x 4.0
17.15 x 1.65
17.15 x 3.20
18.0 x 1.0
18.0 x 1.50
18.0 x 2.0
18.0 x 2.50
18.0 x 3.0
18.0 x 4.0
20.0 x 1.0
20.0 x 1.5
20.0 x 2.0
20.0 x 2.5
20.0 x 3.0
20.0 x 4.0
20.0 x 5.0
22.0 x 1.0
22.0 x 1.5
22.0 x 2.0
22.0 x 2.5
22.0 x 3.0
25.0 x 1.0
25.0 x 1.5
25.0 x 3.0
25.0 x 4.0
25.0 x 5.0
28.0 x 1.0
28.0 x 2.0
28.0 x 2.5
28.0 x 3.0
28.0 x 4.0
28.0 x 5.0
30.0 x 1.50
30.0 x 2.0
30.0 x 2.50
30.0 x 4.0
30.0 x 5.0
35.0 x 1.50
35.0 x 2.0
35.0 x 2.50
35.0 x 5.0
38.0 x 2.0
38.0 x 2.5
38.0 x 3.0
38.0 x 4.0
38.0 x 5.0
42.0 x 2.0
42.0 x 3.0

 

Chemische Zusammensetzung

Grad C Si Mn P S Cr Ti Ni
X 6 CRNIMOTI 17 12 2 0.08 max 1.00 max 2.0 max 0.045 max

0.015

19.0

 0.7 max 13.5 max

 

 

Physikalische Eigenschaften

Das Material nach DIN EN 1.4571 (X6CrNiMoTi17-12-2) wird durch Zugabe von Titan (Ti) zu Edelstahl EN 1.4401 (X5CrNiMo17-12-2) hergestellt, um die Korrosionsbeständigkeit zu erhöhen. Titan kann die Korrosionsbeständigkeit von Edelstahl, insbesondere die interkristalline Korrosion, erhöhen, die Empfindlichkeit von Edelstahl wirksam verhindern und auch die Stabilität von Stahl bei hohen Temperaturen und hohem Druck erhöhen. Wenn das Massenverhältnis von Titan zwischen 0,03% und 0,1% liegt, steigt die Streckgrenze von Stahl. Daher weist das Material nach EN 1.4571 eine höhere Temperatur, Korrosionsbeständigkeit und Suszeptibilitätsbeständigkeit als 1.4401 auf.